Titanium grade 2-4 crowns and bridges

 

State-of-the-art 5-axis HSC milling machines mill the individual frames from the DMC blanks .

 

Even complicated geometries with undercuts or diverging dies can be produced according to the individual ideas of the dental technician.

 

Titan Implantatbrücke

 

Alloy type : DMC-Titanium Grade 5

 

Vickers hardness 350 HV 5/30

CTE value (25-500° C) 10.3 * 10-6 K-1

Mass contents Aluminum: 5.5 - 6.75 % Vanadium: 3.5 - 4.5 % Other: < 0.4 % Rest: titanium

Tensile strength 930 MPa / 0.2 % Yield strength 900 MPa/ elongation at break 10 %.

melting point 1604 - 1660 °C

 

 

Alloy type : DMC- Titanium Grade 2

 

Type 3 according to ISO 16744

Vickers hardness 150 HV 5/30

CTE value (25-500 °C) 9.6 * 10-6 K-1

Mass contents Ti > 99 %.

Tensile strength 345 MPa / 0.2 % proof stress 275 MPa / elongation at break 20 % / density 4.51g/cm3

melting point 1660 °C